Characterization of Nb3Sn Coated Nb Samples |
| Authors |
- Y. Trenikhina, S. Posen, A. Romanenko
Fermilab, Batavia, Illinois, USA
- D.L. Hall
Cornell University (CLASSE), Cornell Laboratory for Accelerator-Based Sciences and Education, Ithaca, New York, USA
- M. Liepe
Cornell University, Ithaca, New York, USA
|
| Abstract |
Nb3Sn has a great potential to replace traditional Nb for the fabrication of SRF cavities. The higher critical temperature of Nb3Sn potentially allows for an increased operational temperature for SRF cavities, which promises cryogenic cost savings. We present preliminary characterization of Nb3Sn layer grown on flat Nb sample prepared by the same chemical vapor deposition method that is used for the cavity coating. SEM, TEM/EDS, TEM imaging and diffraction characterization was used in order to evaluate any chemical and structural defects that could be responsible for the limited quench field and high residual resistance. Variation of local stoichiometry was found in the Nb3Sn layer, which is in line with previous studies. Regions of decreased Sn content can have a lower Tc in comparison to the stoichiometric composition, which may be responsible for the limited performance. AES investigations of the Nb3Sn surface before and after HF-rinse were done in order to explore the mechanism that is responsible for the performance degradation of HF-rinsed Nb3Sn coated cavities.
|
| Paper |
download TUPB056.PDF [0.842 MB / 4 pages] |
| Conference |
SRF2015, Whistler, BC, Canada |
| Series |
International Conference on RF Superconductivity (17th) |
| Proceedings |
Link to full SRF2015 Proccedings |
| Session |
Poster Session |
| Date |
15-Sep-15 14:30–17:40 |
| Main Classification |
Fundamentals SRF R&D - Other Materials |
| Keywords |
SRF, electron, cavity, ion, niobium |
| Publisher |
JACoW, Geneva, Switzerland |
| Editors |
Robert E. Laxdal (TRIUMF, Vancouver, BC, Canada); Jana Thomson (TRIUMF, Vancouver, BC, Canada); Volker RW Schaa (GSI, Darmstadt, Germany) |
| ISBN |
978-3-95450-178-6 |
| Published |
December 2015 |
| Copyright |
|